치과용 도재의 균열전파 특성과 도재 - 금속간의 응력분석
An evaluation of the crack propagation characteristics of porcelain and the bond stress of ceramo-metal system
박주미, 배태성, 송광엽, 박찬운,
소속 상세정보
박주미 ( Park Ju-Mi ) - 전북대학교 치과대학 치과보철학교실
배태성 ( Bae Tae-Sung ) - 전북대학교 치과대학 치과재료학교실
송광엽 ( Song Kwang-Yeob ) - 전북대학교 치과대학 치과보철학교실
박찬운 ( Park Charn-Woon ) - 전북대학교 치과대학 치과보철학교실
KMID : 0362419940320010047
Abstract
This study was carried out to evaluate the effect of the crack propagation characteristics and bond stress of ceramo-metal system. In order to characterize the crack propagation, the static crack propagation stored in 37℃distilled water of two
commerical porcelains and the dynamic crack propagation under cyclic flexure load of ceramo-metal system were examined. In order to characterize the bond stress, the shear bond test, the 3-point flexure bond test, and the finite element stress analysis of ceramo-metal system were conducted. @ES The results obtained were as follows: @EN 1. Bulk densities and Young’s moduli of opaque porcelains increased with repeated firing. 2. Maximum fracture toughness during 4 firing cycles showed at the group of 4 firing cycles in Ceramco porcelain and 2 firing cycles in Vita porcelain. 3. Shear bond strength and flexure bond strength of Ceramco-Verabond specimen were larger than those of Ceramco-Degudent G specimen(p<0.05) 4. Interfacial stresses under three point flexure bond test were concentrated at the edges of ceramometal system. 5. When a cyclic flexure load was applied, the crack growth rate of porcelain surface of ceramometal specimens was decreased as load cycles increased.