잇솔질과 열처리가 세로머의 색안정성에 미치는 영향
Color stability of ceromers after thermocycling and brushing
이양진, 조리라,
소속 상세정보
이양진 ( Yi Yang-Jin ) - 강릉대학교 치과대학 치과보철학교실
조리라 ( Cho Lee-Ra ) - 강릉대학교 치과대학 치과보철학교실
KMID : 0362420010390010037
Abstract
Ceromers, new indirect resin system, are now being adopted for esthetic restorations. Despite of its translucency and good color matching, color stability after long-term use wart unknown till now. This in vitro study was designed to evaluate color stability of some ceromers when subjected to brushing after thermocycling. Three types of ceromers: Sculpture, Targis, Artglass and a direct resin system, Z100 were prepared to disks 12 mm in diameter, 2.5 mm in thickness. All specimens were polished, and Sculpture and Targis specimens were divided to two groups, respectively. Then, half of them were glazed according to manufacturer’s instructions. All specimens were brushed 20,000 times after 10,000 cycle thermocycling. Color was measured with spectrophotometer after 1,000, 3,000, 10,000 times thermocycling and 20,000 time brushing, respectively. Color difference(ΔE) was calculated according to CIE LAB system. During thermocycling, Sculpture & Targis system with polished surface showed greater color change than any other groups. After brushing, color difference was reduced significantly. Mean values of ΔE ranged 0.98 to 2.98. All Ceromers were considered clinically acceptable after thermocycling and brushing, and color change mechanism was affected by the brands and finishing methods. It might be concluded that color change of ceromer is due to surface alteration.
키워드
Brushing; Ceromer; Color; Glazing; Polishing; Stability; Thermocycling
원문 및 링크아웃 정보
등재저널 정보