나노 크기 탄산인회석을 함유한 치약의 상아세관 폐쇄효과 및 지속력 평가
Occluding effect of dentinal tubule and sustaining power with dentifrice containing nano-carbonate apatite
이수영, 권호근, 김백일,
소속 상세정보
이수영 ( Lee Su-Young ) - 남서울대학교 치위생학과
권호근 ( Kwon Ho-Keun ) - 연세대학교 치과대학 예방치과학교실
김백일 ( Kim Baek-Il ) - 연세대학교 치과대학 예방치과학교실
KMID : 0355420110350040388
Abstract
Objectives: The aim of this study was to evaluate the occluding effect of dentinal tubule and sustaining power with dentifrice nano-carbonate apatite in vitro.
Methods: In the first test, fifty dentin specimens were divided randomly into the following five groups; control group (baseline), experimental group (20% n-CAp), negative control group (0% n-CAp), and positive control groups (1: 10% SrCl2 and 2: Er:Cr:YSGG laser). The specimens of each group were brushed for 50 strokes with a V8 Cross Brushing Machine or laser irradiation for 90 seconds. In the second test, the dentin specimens of four groups except the control group were immersed in demineralization solution (pH 4.8) for 3, 5, and 10 min after the first test. All the specimens were evaluated by SEM and quantified using an image analyzer. The results were analyzed by one-way ANOVA and Tukey’s post hoc analysis using the SPSS 12.0 statistical package program.
Results: The 20% n-CAp group showed an occluding rate of 78% and significantly higher occlusion effects than the 0% n-CAp group, 10% SrCl2 group and Er:Cr:YSGG laser group (p＜0.05). When immersed in acid solution for 3 min, the size of the dentinal tubule not almost increased (ED Highlight - meaning is completely unclear) in 20% n-CAp group and Er:Cr:YSGG group. These groups showed significantly higher sustaining power than the 0% n-CAp group (p＜0.05). However, there was a no significant difference in immersion time for 5 and 10 min.
Conclusions: The dentifrice containing 20% n-CAp was the most effective in occluding the dentinal tubules and showed superior sustaining power in the short-term.
키워드
나노 탄산인회석; 상아세관 폐쇄효과; 상아질 지각과민증; Er:Cr:YSGG 레이저
dentin hypersensitivity; Er:Cr:YSGG Laser; nano-carbonate apatite; occlusion effect