치과용 의치상 아크릴릭 레진 단량체 중량비에 따른 기계적 성질
The mechanical property investigation according to the monomer weight ratio of the dental acrylic denture base resin
이희경, 선금주,
소속 상세정보
이희경 ( Lee Hee-Kyung ) - 대구보건대학 치기공과
선금주 ( Sun Gem-Ju ) - 광주보건대학교 치기공과
KMID : 0362120130350040287
Abstract
Purpose: This study is to provide basic data of the dental acrylic denture base resin in the mechanical property difference investigation according to the monomer composition weight ratio of the acrylic denture base resin.
Methods: The monomer composition of the acrylic denture base resin and weight ratio makes the different specimen. It measured the mechanical property with the specimens through Hardness Test, Tensile Test, Flexural Test, Flexural Modulus, FT-IR Test.
Results: The control group Vertex was 18.4 Hv and the experimental group MED was 14.46~19.07Hv in the hardness test. Vertex was 364N, MED-3 was lowest in the tensile strength test and the Head of a family cursor declination was big. The result declination of the experimental specimens showed. Vertex and MED-2 was the highestest in the flexural test and after coming MED-6, MED-5, MED-1, MED-3, MED-4. Vertex and MED-2, as to a spectrum for 500~1800 -1 peak can show the excellent degree of polymerization in the FT-IR Test.
Conclusion: The ideal weight ratio of the monomer of the acrylic denture base resin of which the mechanical property is the highestest was MMA 100g, EDGMA 5g, DMA 0.2g, of MED-2.
키워드
PMMA; MMA; Denture; Acrylic Resin; Flexural test