3D 프린팅용 UV 경화 수지의 조사량 및 항온수조 침적에 따른 수축률의 차이

Difference between shrinkage rate of irradiation amount of 3D printing UV curable resin and shrinkage rate according to a constant temperature water bath

대한치과기공학회지 2020년 42권 2호 p.113 ~ 120
김동연,
소속 상세정보
김동연 ( Kim Dong-Yeon ) - 4RD Dental Laboratory

Abstract


Purpose: This study is to compare and analyze the shrinkage of the specimen after UV irradiation of UV cured resin at 5, 15, and 30 minutes.

Methods: A cylindrical UV cured specimen was produced using a stainless steel mold. UV cured resin specimens were prepared in three groups: 5 minutes cured (5M), 15 minutes cured (15M), and 30 minutes cured (30M). The measurement was made in total 3rd. The measurement was made in total 3rd. The primary measurement was made after 24 hours using a digital measuring instrument. The 2nd and 3rd measurements were deposited in a constant temperature water bath and the shrinkage was measured. The measured data was calculated by referring to the ASTM C326 linear measurement calculation method. T-test and One-way ANOVA were performed to test the significance between groups. The post-test was conducted with Tukey (α=0.05).

Results: When the inner diameter and the outer diameter of the three groups not placed in the water bath were compared and analyzed, the contraction was the smallest at 6.8% in the 5M group, and the contraction was the largest at 7.3% in the 30M group. In the outer diameter, the contraction of the 5M group was the smallest at 3.5%, and the contraction of the 30M group was the largest at 4.5%. Shrinkage decreased in all three groups immersed in a water bath for 3-7 days.

Conclusion: In the UV cured resin specimen, the shrinkage increased as the amount of UV irradiation increased.

키워드

UV; Curing; Resin; Shrinkage