Die spacer의 두께에 따른 복합레진 inlay 의 치은 변연부 미세누출 및 접착양태에 관한 연구
Gingival margial leakage and bonding pattern of the composite resin inlay according to various thickness of die spacer
박태일, 신동훈, 홍찬의,
소속 상세정보
박태일 ( ) - 단국대학교
신동훈 ( ) - 단국대학교
홍찬의 ( ) - 단국대학교
KMID : 0362319950200010152
Abstract
This experiment was performed to observe the adhesion pattern and microleakage in the gingival margin according to variation in the resin cement thickness which results from thickness of Die spacer, which is considered to effect the adaptability
of
the
composite resin inlays. Clearfil CR inlays were fabricated on stone models with CR Sep applicated once and Nice fit twice, 4 times, and 6 times each. After 2nd curing within the CRC-100 oven, CR inlays were cemented with CR inlay cement. Dye(2%
methylene blue) penetration and adhesion pattern were evaluated after sectioning of gingival margin into 3 pieces.
@ES The results were as follows;
@EN 1. The thickness of resin cement showed unevenchanging pattern with that of die spacer, namely, it was increased until 4 times' application of Nice-Fit but was decreased with 6 times' application of that.
2. The degree of dye penetration wasn't affected by cement thickness within a limited value.
3. Most of dye penetration was shown through the interface between cement and enamel rather than the interface between cement and CR inlay. This shows that the affinity of resin cement for CR inlay was superior to the adhesive strength with
tooth
structure.
4. No gap was found at the interface between enamel and cement but some showed separation between dentin and cement. It is concidered that the contraction force of cement was less than the bond strength with the enamel.
5. Lots of voids were found in the CR inlay and resin cement. There was a pooling tendency of bonding agent and cement in the axiogingival line angle portion.
6. In some specimens, cracks were shown in enamel margin. From this it could be considered that cavity preparation and surface treatment weakened the tooth structure.