강화형 글라스 아이오노머 합착용 시멘트의 접합강도 및 변연누출에 대한 연구
COMPARISON OF SHEAR BOND STRENGTH AND MARGINAL LEAKAGE OF RESIN MODIFIED GLASS IONOMER CEMENTS
박혜양, 오남식, 이근우, 이호용,
소속 상세정보
박혜양 ( Park Hye-Yang ) - 연세대학교 치과대학 치과보철학교실
오남식 ( Oh Nam-Sik ) - 연세대학교 치과대학 치과보철학교실
이근우 ( Lee Keun-Woo ) - 연세대학교 치과대학 치과보철학교실
이호용 ( Lee Ho-Yong ) - 연세대학교 치과대학 치과보철학교실
KMID : 0362419970350040647
Abstract
The resin modified glass ionomer cements(RMGICs) have been used for years since 1989. Recently it has been developed for luting of fixed restorations. To evaluate the bond strength and marginal leakage of RMGICs for luting usage, the 80 extracted human molars which had uniform area of exposed dentin were cemented with 3 types of RMGICs(Fuji Duet, Advance, Vitremer), a conventional Glass Ionomer Cement(GIC-Fuji I), and a resin cement (Panavia 21) to base metal alloy(Ni-Cr-Be). After thermocycling the specimens were immersed in basic fuschin dye for measuring marginal leakage. The shear bond strength was measured with Instron and the maximum dye penetration was measured to 0.1mm. The type of fractured patterns were determined with stereoscope (x7.5). The results are as follows. 1. The difference between 3 RMGICs and a conventional GIC in shear bond strength was not statistically significant. It seemed that RMGICs had lower shear bond strength than resin cement. (p<0.01) 2. The mean scores of marginal leakage had no significant difference between the resin cement and 3 RMGICs but it was much higher in conventional GIC than the RMGICs (p<0.05) 3. It was determined that the manufacturer and the methods of dentin pretreatment determined the pattern of fracture surface and the frequency of adhesive failure between teeth and 3 RMGICs standed as in following order - Vitremer, Advance, Fuji Duet. (p<0.01) When the fracture pattern was analyzed, it could be said that the materials and the method of dentin pretreatment have much effect on bonding states. This means that the dentin bonding agents should be improved. But the limited products in this experiment can not evaluate the physical properties of the entire RMGICs. Therefore a further study which can evaluate various RMGICs should be in progress to develop better cements.
키워드
Resin modified glass ionomer cement;Resin cement;Chemical cure;Dual cure;Shear bond strength;Marginal leakage