치아표면 처리방법과 themocycling이 콤포짓트 레진 코어의 미세누출에 미치는 영향
THE EFFECTS OF SURFACE TREATMENT AND THERMOCYCLING ON THE MICROLEAKAGE OF COMPOSITE RESIN CORES
임용철, 진태호,
소속 상세정보
임용철 ( Lim Yong-Chul ) - 원광대학교 치과대학 치과보철학교실
진태호 ( Jin Tai-Ho ) - 원광대학교 치과대학 치과보철학교실
KMID : 0362420000380020255
Abstract
The purpose of this study was to compare the microleakage of the composite resin cores according to surface treatment, dentin bonding agents, and thermocycling. For this study, 120 extracted premolar teeth were used. Flat occlusal surfaces were prepared with diamond disk, and treated with air-abrasion, acid-etching, combination. The composite resin core was built with Z-100 after application of Scotchbond Multi-Purpose and All-Bond 2. Prepared specimens were thermocycled for 2,000 cycles. Specimens were immersed in 1% methylene blue solution for 24hours at 371C. The microleakage was measured with a inverted metallurgical microscope(BHS313, Olympus, Japan). The following conclusions were drawn from this study 1. The microleakages in the groups treated with air-abrasion and with acid etching were greater than that of the groups treated with combination method before thermocycling(p<0.05), the microleakages of the groups treated with air-abrasion were greater than that of the groups treated with acid-etching and combination method after thermocycling(p<0.05). 2. There were no significant difference between groups using Scotchbond Multi-Purpose and the groups using All-Bond 2. 3. Thermocycling didri t affect the change of microleakage in all cases.
키워드
원문 및 링크아웃 정보
등재저널 정보