Degassing 조건이 Ni-Cr 합급의 도재결합력에 미치는 영향
EFFECT OF DEGASSING CONDITION ON CERAMIC BOND STRENGTH OF Ni-Cr ALLOYS
이은화, 전유진, 전윤경, 임장섭,
소속 상세정보
이은화 ( Lee Eun-Hwa ) - 부산대학교 치과대학 치과보철학교실
전유진 ( Jeon You-Jin ) - 부산대학교 치과대학 치과보철학교실
전윤경 ( Jeon Yun-Kyung ) - 부산대학교 치과대학 치과보철학교실
임장섭 ( Lim Jang-Seop ) - 부산대학교 치과대학 치과보철학교실
KMID : 0362420000380040461
Abstract
This study evaluated the effect of dagassing on the ceramic bond strength of two Ni-Cr alloys under varying holding time at the upper limit temperature and atmospheric conditions. Metal specimens were divided into 5 groups for each alloy according to degassing conditions prior to porcelain application : no degassing, degassing under vacuum without hold, degassing under vacuum with hold for 5min. and 10 min. respectively at the upper limit temperature and degassing in air. Total number of metal ceramic specimens was eighty and each group had eight specimens : The ceramic bond strength was measured by four-point flexural test using Instron and the fractured surface was examined under SEM. The results obtained were as follows. 1. Degassing in air improved the ceramic bond strength of Ni-Cr alloys. 2. In degassing under vacuum, hold at the upper limit temperature was advantageous to the ceramic bonding of Ni-Cr alloys. 3. After ceramic metal bond test, metal surfaces were partially covered with the thin porcelain layer, and the cohesive failures in porcelain were predominant in groups showing higher ceramic bond strength.
키워드
원문 및 링크아웃 정보
등재저널 정보