반복 하중이 Full veneer crown의 유지력에 미치는 영향에 관한 연구
THE EFFECT OF CYCLIC LOADING ON THE RETENTIVE STRENGTH OF FULL VENEER CROWNS
김기연, 이선형, 정헌영, 양재호, 허성주,
소속 상세정보
김기연 ( Kim Ki-Youn ) - 서울대학교 치과대학 치과보철학교실
이선형 ( Lee Sun-Hyung ) - 서울대학교 치과대학 치과보철학교실
정헌영 ( Chung Hun-Young ) - 서울대학교 치과대학 치과보철학교실
양재호 ( Yang Jae-Ho ) - 서울대학교 치과대학 치과보철학교실
허성주 ( Heo Seong-Joo ) - 서울대학교 치과대학 치과보철학교실
KMID : 0362420000380050583
Abstract
Dislodgement of a crown or extension bridge and the loosening of a retainer of a bridge is a serious clinical problem in fixed restoration. Generally these problems are considered to be associated with deformation of the restoration. During biting, the restoration is subjected to complex forces and deforms considerably within the limit of its elasticity. Deformation of the restoration under the occlusal force induces excessive stress in the cement film, which then leads to the cement fracture. Such a fracture may eventually cause loss of the restoration. Because most of the past retention tests for full veneer crown were done without fatigue loading, they were not exactly simulating intraoral environment. And the purpose of this study was to evaluate the effect of cyclic cantilever loading on the retentive strength of full veneer crowns depending on different type of cements and taper of prepared abutment. Steel dies with 8degrees or 16degrees convergence angle were fabricated through milling and crowns with the same method. These dies and crowns were divided into 8 groups. Group 1: 16degrees taper die, cementation with zinc phosphate cement, without loading Group 2: 16’taper die, cementation with zinc phosphate cement, with loading Group 3: 8degrees taper die, cementation with zinc phosphate cement, without loading Group 4: 8degrees taper die, cementation with zinc phosphate cement, with loading Group 5: 16degrees taper die, cementation with Panavia 21, without loading Group 6: 16degrees taper die, cementation with Panavia 21, with loading Group 7: 8degrees taper die, cementation with Panavia 21, without loading Group 8: 8degrees taper die, cementation with Panavia 21, with loading After checking the fit of die and crown, the luting surface of dies and inner surface of crowns were air-abraded for 10 seconds. The crowns were cemented to the dies, with cements mixed ac cording to the manufacturer’ s recommendations. A static load of 5 kg was then applied for 10 min utes with static loading device. Twenty-four hours later, group 1,3,5,7 were only thermocycled, group 2,4,6,8 were subjected to cyclic loading after thermocycling. Retentive tests were performed on the Instron machine. From, the finding of this study, the following conclusions were obtained. 1. Panavia 21 showed significantly higher retentive strength than zinc phosphate cement for all groups(p<0.05). 2. There was a significant difference in the retentive strength between 8degrees and 16degrees taper for zinc phosphate cement(p<0.05), but no significant difference for Panavia 21(p>0.05). 3. Cyclic loading significantly decreased the retentive strength for all groups (p<0.05) . 4. For zinc phosphate cement, there was 35% reduction of the retentive strength after loading in the 16degrees taper die, 25% in the 8degrees taper die, and for Panavia 21, 21% in the 16degrees taper die, 18% in the 8degrees taper die.
키워드
Cyclic loadig;Taper;Luting cement;Retentive strength