실험용 불소바니쉬가 우치의 비커스 경도에 미치는 영향
Effect of Experimental Fluoride Varnish upon the Vickers Hardness of Bovine Teeth
김아진, 손주리, 오승한, 배지명,
소속 상세정보
김아진 ( Kim Ah-Jin ) - 서라벌대학교 치위생과
손주리 ( Son Ju-Lee ) - 원광대학교 치과대학 치과생체재료학교실
오승한 ( Oh Seung-Han ) - 원광대학교 치과대학 치과생체재료학교실
배지명 ( Bae Ji-Myung ) - 원광대학교 치과대학 치과생체재료학교실
KMID : 1035320160430010081
Abstract
The purpose of this study was to evaluate the effect of the experimental and commercial fluoride varnishes on the Vickers hardness of bovine teeth. The experimental fluoride varnishes with 5 wt.% NaF were fabricated using Bis-GMA or rosin as the resin base. The components were mixed with over-head stirrer under warming up in a double boiler for 30 minutes. Four commercial fluoride varnishes (V-varnish, Flor-opal, Cavity shield, Fluor protector) were compared with the experimental fluoride varnishes. Vickers hardness was measured on the labial surface of bovine anterior teeth after applying fluoride varnish on 5th and 30th day. The surface of bovine teeth was observed with a scanning electron microscope before and after applying fluoride varnish and the change of the components on the bovine teeth surface was measured with EDX. In terms of hardness, the experimental rosin-based fluoride varnish showed significantly higher hardness on the 5th and 30th day than the control (bovine teeth without fluoride treatment)(p<0.05). EDX results showed that the fluoride content on the surface of bovine teeth treated with the experimental rosin-based fluoride varnish was highest on the 1st and 10th day. The higher hardness and fluoride content of experimental rosin-based fluoride varnish can be considered to be used as an effective fluoride varnish to prevent dental caries.
키워드
Fluoride varnish; Vickers hardness; bis-GMA-based; Rosin-based
원문 및 링크아웃 정보
등재저널 정보