글레이즈 처리한 다색 리튬 디실리케이트와 지르코니아의 색조비교
Color comparison of glaze-treated multi-coloured lithium disilicate and zirconia
황별, 지정희, 박철수, 신재우, 이정환, 이민호, 배태성,
소속 상세정보
황별 ( Hwang Byeol ) - Chonbuk National University School of Dentistry Department of Dental Biomaterials
지정희 ( Ji Jeong-Hui ) - Chonbuk National University School of Dentistry Department of Dental Biomaterials
박철수 ( Park Cheol-Soo ) - Chonbuk National University School of Dentistry Department of Orthodontics
신재우 ( Shin Jae-Woo ) - Chonbuk National University School of Dentistry Department of Dental Biomaterials
이정환 ( Lee Jung-Hwan ) - Gwangju Health University Department of Dental Laboratory Technology
이민호 ( Lee Min-Ho ) - Chonbuk National University School of Dentistry Department of Dental Biomaterials
배태성 ( Bae Tae-Sung ) - Chonbuk National University School of Dentistry Department of Dental Biomaterials
Abstract
본 연구의 목적은 다색의 지르코니아 블록과 리튬 디실리케이트 블록의 글레이즈 처리가 광학적 특성에 미치는 영향을 조사하는 것이다. 지르코니아계 50% 입방정 함유 Ultra Translucent Multi-Layered (UTML) disc와 리튬 디실리케이트계 Amber Mill Direct (AMD) block을 크라운의 상층부(T), 중앙부(M), 하층부(B)를 상정하여 최종 두께가 1.2 mm가 되도록 준비하였다. 세 종류의 paste glaze (InSyncⓡ Glaze Paste, IPS E.max Ceram Glaze Paste, Amber Ceram G7 Glaze Paste)를 시편의 표면에 균일한 두께로 적용하고 소성하였다. CIE L*, a*, b* 값은 분광 광도계를 사용하여 각 시편의 상층부, 중앙부 및 하층부에서 각각 3회씩 측정하여 분석하였다. HR FE-SEM을 이용하여 모재와 글레이즈 층과의 결합계면을 관찰하였다. 글레이즈 처리한 실험군에서는 L* 값은 증가하고, a* 값과 b* 값은 감소하였다. 무처리 군에서 측정된 반투명도 값은 UTML보다 AMD군에서 통계학적으로 유의하게 더 높았다(P<0.05). 반투명도는 UTML군에서는 글레이즈 처리 전후 유의한 차이를 보이지 않았지만(P>0.05), AMD군의 글레이즈 처리 후 무처리 군에 비해 유의하게 감소되었다(P<0.05). 대조비는 글레이즈 처리 후 무처리 군에 비해 전반적으로 증가한 양상을 보였다. 결론적으로, 글레이즈 처리는 세라믹 수복물 제작의 마지막 단계로서 광학적 특성에 영향을 줄 수 있으므로 치과기공사가 원하는 색조를 재현하고자 할 때 글레이즈의 선택은 중요하게 고려되어야 할 것으로 생각된다.
The purpose of this study was to investigate the effect of glazing treatment of multi-colored zirconia disc and lithium disilicate block on the optical properties. From an Ultra Translucent Multi-Layered (UTML) disc containing 50% cubic crystal and a lithium disilicate-based Amber Mill Direct (AMD) block, the 1.2 mm thick specimens of the upper layer (T), the center (M), and the lower layer (B) were prepared. Three types of paste glaze of InSync Glaze Paste, IPS E.max Ceram Glaze Paste, and Amber Ceram G7 Glaze Paste were applied and fired to a uniform thickness on the surface of the specimen. CIE L*, a*, b* values were measured using a spectrophotometer and contrast and translucency were calculated. The bonding interface with the glaze layer was observed using HR FE-SEM. In the glazed groups, L* value increased, but a* value and b* value decreased. The translucency value measured in the untreated group was statically higher in the AMD groups than in UTML groups (P<0.05). The translucency did not show a significant difference before and after glazing treatment in the UTML group (P>0.05), but significantly decreased compared to the untreated group after glazing treatment in the AMD group (P<0.05). The contrast ratios generally increased after glaze treatment compared to the untreated group. Since the glaze treatment can affect the optical properties of ceramic restorations, the choice of glaze should be considered important for the desired color by the dental technician.
키워드
지르코니아; 리튬디실리케이트; 광학적특성; 글레이즈
Zirconia; Lithium disilicate; Optical properties; Glaze