세 가지 용액에 의한 기혼합형 MTA의 기계 및 물리·화학적 특성 연구
Mechanical and physico-chemical properties of premixed-MTA in contact with three different types of solutions
강태윤, 최지원, 김광만, 권재성,
소속 상세정보
강태윤 ( Kang Tae-Yun ) - Yonsei University College of Dentistry Department of Dental Biomaterials and Bioengineering
최지원 ( Choi Ji-Won ) - Yonsei University College of Dentistry Department of Dental Biomaterials and Bioengineering
김광만 ( Kim Kwang-Mahn ) - Yonsei University College of Dentistry Department of Dental Biomaterials and Bioengineering
권재성 ( Kwon Jae-Sung ) - Yonsei University College of Dentistry Department of Dental Biomaterials and Bioengineering
Abstract
본 연구의 목적은 치수복조 및 근관역충전재 등으로 사용될 수 있는 기혼합형 Mineral trioxide aggregate (MTA; Endocem MTA premixed regular, Maruchi, Gangwon-do, Korea)를 세 가지 유형의 용액; 유사생체용액(simulated body fluid, SBF), 0.9% 생리식염수(saline), 멸균증류수(distilled water, DW)에 7일 동안 침적 후 압축강도, pH, 그리고 표면 양상의 변화를 비교 분석하는 것이다. MTA 시편을 각 용액에 1일과 7일 간 침지 후 만능재료시험기를 이용하여 압축강도를 측정하였다. 이때, 용액에 침지하지 않은 MTA는 대조군으로 설정하였다. pH 분석을 위해, MTA 시편을 각 용액에 침지하여 3, 6, 12, 24, 72시간, 그리고 168시간 후 pH meter를 이용하여 측정하였다. 또한, 각 용액으로 인한 MTA 시편의 표면 양상의 변화를 관찰하기 위해 7일동안 침지 후 SEM-EDS로 분석하였다. 통계 분석은 일원배치분산분 석, Tukey’s test 사후 검정, 그리고 독립 표본 T검정을 시행하였다. 압축강도 측정 결과, 용액에 보관하지 않았던 대조군과 비교 시 모든 군에서 유의한 차이로 증가하였다(p<0.05). 용액 내에 보관 기간이 증가할수록 모든 군에서 유의한 차이로 압축강도가 증가하는 양상을 보인 반면(p<0.05), 용액의 종류에 따른 유의한 차이는 발견되지 않았다 (p>0.05). pH 측정 결과, 모든 그룹에서 침지 기간이 길어질 수록 pH가 높아지는 양상을 보였으며, 모든 시점에서 saline과 DW에 침지한 pH가 SBF에 침지한 pH보다 유의하게 높았다(p<0.05). SEM-EDS 분석 결과, 용액에 침지한 MTA 시편에서 주로 Ca와 Zr가 존재하는 것을 관찰할 수 있었다. 따라서, MTA의 압축 강도에 있어 침적 용액의 종류는 유의한 영향을 미치지 않지만, pH의 조건 및 표면 변화에는 유의한 영향을 미칠 수 있음에 따라 향후 실험 조건 설정과 MTA 제품 개발 시 유용한 정보로 활용될 수 있을 것으로 사료된다.
The study aims to analyze the compressive strength, pH, and surface properties of mineral trioxide aggregates (MTA), which can be used as a pulp capping and root canal filling material. The tests were performed after immersing premixed types of MTA for seven days into three different solutions: simulated body fluid (SBF), saline, and distilled water (DW). A universal testing machine was used to measure the compressive strength after one and seven days of immersion. The un-immersed MTA was used as the control. To investigate the pH variation, MTA specimens were immersed in each solution and the pH was measured using a pH meter after 3, 6, 12, 24, 72, and 168 h. Changes on the MTA surface were also observed by SEM-EDS after seven days of immersion. Moreover, statistical analysis was performed by one-way ANOVA, Tukey's post-hoc test, and independent sample t-test. All experimental groups showed significantly higher compressive strengths compared to the control group (p<0.05). In addition, as the immersion time increased, the compressive strength gradually and significantly increased among all the groups. On the other hand, the difference was insignificant among solutions with the same immersion time (p>0.05). As the immersion time increased, the pH increased among all the groups, and the pH of samples immersed in saline and DW was significantly higher than that in SBF. The MTA surface immersed in each solution for seven days showed precipitates which mainly composed of Ca and Zr ions. Therefore, the type of contact solution does not significantly affect the compressive strength of MTA, but it significantly influences both the pH and surface condition.
키워드
기혼합형 Mineral trioxide aggregate (Premixed type of MTA); 유사생체용액; 생리식염수; 멸균증류수; 압축강도
Premixed-Mineral trioxide aggregate (MTA); Simulated body fluid (SBF); Saline; Distilled water (DW); Compressive strength